|
Electroslag welding (ESW) is a highly productive, single pass welding process for thick (greater than 25 mm up to about 300 mm) materials in a vertical or close to vertical position. (ESW) is similar to electrogas welding, but the main difference is the arc starts in a different location. An electric arc is initially struck by wire that is fed into the desired weld location and then flux is added. Additional flux is added until the molten slag, reaching the tip of the electrode, extinguishes the arc. The wire is then continually fed through a consumable guide tube (can oscillate if desired) into the surfaces of the metal workpieces and the filler metal are then melted using the electrical resistance of the molten slag to cause coalescence. The wire and tube then move up along the workpiece while a copper retaining shoe that was put into place before starting (can be water-cooled if desired) is used to keep the weld between the plates that are being welded. Electroslag welding is used mainly to join low carbon steel plates and/or sections that are very thick. It can also be used on structural steel if certain precautions are observed. This process uses a direct current (DC) voltage usually ranging from about 600A and 40-50V, higher currents are needed for thicker materials. Because the arc is extinguished, this is not an arc process. ==History== The process was patented by Robert K Hopkins in the United States in February 1940 (patent 2191481) and developed and refined at the Paton Institute, Kiev, USSR during the 1940s. The Paton method was released to the west at the Bruxelles Trade Fair of 1950. The first widespread use in the U.S. was in 1959, by General Motors Electromotive Division, Chicago, for the fabrication of traction motor frames. In 1968 Hobart Brothers of Troy, Ohio, released a range of machines for use in the shipbuilding, bridge construction and large structural fabrication industries. Between the late 1960s and late 1980s, it is estimated that in California alone over a million stiffeners were welded with the electroslag welding process. Two of the tallest buildings in California were welded, using the electroslag welding process - The Bank of America building in San Francisco, and the twin tower Security Pacific buildings in Los Angeles. The Northridge earthquake and the Loma Prieta earthquakes provided a "real world" test to compare all of the welding processes. The Structural Steel welding industry is well aware that, over one billion dollars in crack repairs were needed, after the Northridge earthquake, to repair weld cracks propagated in welds made with the gasless flux cored wire process. Not one failure or one crack propagation was initiated in any of the hundreds-of-thousands of welds made on continuity plates welded with the Electroslag welding process. The History Of Electroslag Welding For High Rise Building And Bridges However the Federal Highway Administration (FHWA) monitored the new process and found that electroslag welding, because of the very large amounts of confined heat used, produced a coarse-grained and brittle weld and in 1977 banned the use of the process for many applications. The FHWA commissioned research from universities and industry and Narrow Gap Improved Electro Slag Welding (NGI-ESW) was developed as a replacement. The FHWA moratorium was rescinded in 2000. 抄文引用元・出典: フリー百科事典『 ウィキペディア（Wikipedia）』 ■ウィキペディアで「Electroslag welding」の詳細全文を読む スポンサード リンク
|